Removal of emerging micropollutants from water using hybrid material precursor to natural sericite clay
The occurrence of a wide range of micropollutants in natural aquatic environment has been reported in different parts of the world. These compounds are harmful for the aquatic life and human beings. Diclofenac and clofibric acid are the two common toxic micropollutants due to very large production and high consumption by humans. The present communication addresses the removal of diclofenac and clofibric acid from aqueous solutions using the hybrid material obtained by incorporating 3-aminopropyltriethoxysilane (APTES) onto the activated sericite clay. Initially, sericte clay was treated for activation and further modified with organosilane to obtain hybrid material. The materials were characterized using SEM, BET surface area, XRD, and FT-IR analyses.SEM and BET surface area analyses showed that the textural property of sericite clay was greatly changed after activation and the surface area was immensely increased from 3.65 to 62.92 m2/g. The organosilane was anchored on the activated clay and confirmed with FTIR analysis. Batch adsorption experiments showed that the diclofenac and clofibric acid removal is maximum at pH 6.0 to7.0 and the adsorption of these two micropollutants were observed to be very fast and the time dependent adsorption data were best fitted to pseudo-second order kinetic model. The maximum adsorption capacity of diclofenac and clofibric acid using APTES-sericite hybrid material was found to be 1.868 and 1.749 mg/g, respectively. Furthermore, the loading capacities of the column packed with APTES-sericite hybrid material were found to be 0.789 and 1.095 mg/g. Therefore, this study indicated that the APTES-sericite hybrid material must be an useful material for the effective removal of diclofenac and clofibric acid from aqueous waste.
Hybrid material; Mesopore; Micropollutants; Organosilane; Sericite
Full Text: PDF (downloaded 469 times)
- There are currently no refbacks.