Effect of MoO3 in the cathode buffer layer on the behaviour of layered organic solar cells

El Assad Zemallach Ouari, Kadda ; El Jouad, Zouhair ; Benchouk, Keireddine ; Kouskoussa, Belkacem ; Cattin, Linda ; Makha, Mohammed ; Khelil, Abdelbacet ; Morsli, Mustapha ; Addou, Mohammed ; Bernède, Jean christian


The behaviour of small-molecule organic solar cells based on copper-phthalocyanine/fullerene with different cathode buffer layer is investigated as a function of air exposure duration. The effect of MoO3 on the properties of photovoltaic solar cells (OPVCs) when it is introduced in the cathode buffer layer (CBL), has been studied. Photovoltaic performances were measured as a function of time of air exposure. During the first days of air exposure, the efficiency of the OPVCs with MoO3 in their CBL increases significantly, while it decreases immediately after air exposure in the case of reference OPVCs, i.e. without MoO3 in the CBL. Nevertheless, the lifetime of the OPVCs with MoO3 in their CBL is around 60 days, while it is only 10 days in the case of reference OPVCs. The initial increase of the OPVC with MoO3 in their CBL is attributed to the slow decrease of the work function of MoO3 due to progressive contamination. Then, the progressive degradation of the OPVCs efficiency is due to water vapour and oxygen contamination of the organic layers. The use of double CBL, Alq3/MoO3, allows to interrupt the growth of pinholes, defects and increases the path of permeating gas. Also it can prevent the contamination of the organic layer by Al. All this results in significant increase of the lifetime of the OPVCs.


Interfaces; Organic compounds; Oxides; Vacuum deposition; Ageing, Electrical properties

Full Text: PDF (downloaded 1921 times)


  • There are currently no refbacks.
This abstract viewed 2267 times