Vacuum Oxy-nitro carburizing of tool steels: structure and mechanical reliability

Nikolova, Maria ; Nikolov, Danail ; Yankov, Emil ; Derin, Bora ; Topalski, Slavcho


AISI H10, H11, H21, and D2 have been vacuum oxy-nitrocarburizing at 570 °C in cycling gas flow manner. Metastable diagram calculations belonging to Fe-N-C and Fe-N-C-X systems (X = Cr, Mo, W), have been performed by using “phase diagram” module of FactSageto predict the steels’ phase compositions. The reactive diffusion of both N and C into the tempered martensite has been discussed on the base of different chemical composition, size, and distribution of phases in the microstructure. The compound layers consisted mainly of not pre-saturated and poreless ε-carbonitride and magnetite (Fe3O4). In D2 steel, nitrogen diffusion caused a complete transformation of the primary carbides in 50 μm depths from the surface affecting the growth of grain boundary carbides. In contrast to the sharp compound/diffusion layer interface of H10, H11, and D2 steels, in H21 carbon and nitrogen were deeply absorbed in the diffusion layer while chromium strongly increased underneath the surface. The vacuum process enhanced the hardness and decreased the friction coefficients down to 0.13-0.15 at 100 N normal load for all samples. Since the compound layer thickness was relatively small for all tool steels, the phase composition and structure of the diffusion layers were found to be crucial for the scratch wear performance.


Thermochemical modeling, SEM, Phase composition, GDOES, Microhardness, Scratch test

Full Text: PDF (downloaded 462 times)


  • There are currently no refbacks.
This abstract viewed 805 times