Effect of pre-weld tempers on mechanical and microstructural behavior ofdissimilar friction stir welds of AA2014 and AA7075

Kumar, Raj ; Upadhyay, Vikas ; Sharma, Chaitanya


In this work, friction stir welding of AA2014 and AA7075 has beenperformed indifferent combinationsof T6 and Otemperto study the influence of base metal temper on microstructure, mechanical properties, and fracture behavior ofdeveloped welds. Four dissimilar welded joints have been developed using optimum process parameters:AA2014-T6 withAA7075-T6, AA2014-O with AA7075-T6, AA2014-T6 with AA7075-O, and AA2014-O with AA7075-O. The stirzonemicrostructurehas been dominated by the base metal placed on the advancing side and hasequiaxed grains withoutconstituent particles. Weld joints' strengthhas beeneither nearly equal or higher than that of low strength base metal,whereasthe weld failure has takenplace from the base metal region when at least one base metal was in O temper and from Stir Zone(SZ) when base metal was in T6 temper.


Friction Stir Welding, Dissimilar aluminum alloys, Pre-weld Temper, Mechanical properties, Microstructure

Full Text: PDF (downloaded 164 times)


  • There are currently no refbacks.
This abstract viewed 247 times